STUDY OF THE PROPERTIES OF MORTAR INCORPORATED FROM MELTED PLASTIC BAGS
- Laboratoire Chimie Organique et Sciences de lEnvironnement (LaCOSE), Faculte des Sciences et Techniques (FaST), Universite de Kara, BP 404 Kara-TOGO.
- Laboratoire de Recherche en Sciences de lIngenieur, Ecole Polytechnique de Lome (EPL), Universite de Lome, BP 1515, Lome-TOGO.
- Abstract
- Keywords
- Cite This Article as
- Corresponding Author
The aim of this research is to study the physical-mechanical behaviour and durability of mortars containing melted plastic bags. To this end, 4cmx4cmx16cm test specimens of mortar containing cement or not and melted plastic bags at a mass ratio ranging from 10 to 25% of the mixture were produced. Compressive strength, flexural strength and acid durability were measured. The results show that the quantity of plastics in the mortars is inversely proportional to water absorption. Similarly, cementless mortars containing 25% plastic bags (MWC25) and cement mortars containing 25% plastic bags (CM25) gave maximum compressive strengths of 9.45MPa and 10.45MPa respectively. The durability test in a 5% sulphuric acid solution showed that CM25 and MWC20 lost 50% of their mass after 28 days.
[Komi Jean-Marcel AMEWOUAME, Kwamivi N. SEGBEAYA, Yaovi Agbeko KOUTO and Yawovi M. X. Dany AYITE (2024); STUDY OF THE PROPERTIES OF MORTAR INCORPORATED FROM MELTED PLASTIC BAGS Int. J. of Adv. Res. (Jul). 66-74] (ISSN 2320-5407). www.journalijar.com
Laboratoire Chimie Organique et Sciences de l’Environnement (LaCOSE), Faculté des Sciences et Techniques (FaST), Université de Kara, BP 404 Kara-TOGO ; et Laboratoire de Recherche en Sciences de l’Ingénieur, Ecole Polytechnique de Lomé (EPL), Université de Lomé, BP 1515, Lomé-TOGO
Togo